I have a vortech supercharger and I was wondering was it a bad idea to powder coat jus curious is it possible or would it mess it up???
|
2stangs69-91
Member # 1951
|
posted
Why would it mess it up? Only thing I could think of is it retaining more heat now. Another question why you asking this now after it is already powder coated?
|
JohnB
Member # 969
|
posted
I hope it was sealed up REALLY well prior to coating. Not to mention how hot was it cooked during the coating process? Anything more than 250-275* may have hurt a seal or two...
|
Nasty Notch
Member # 8863
|
posted
Haven't powder coated yet but that thing bout reataing heat sounds like the perfect reason y I wount be doing it thanks u guys always helpful!
|
JohnB
Member # 969
|
posted
Find someone that does polishing. They look great after they are buffed out!
|
copcar
Member # 10113
|
posted
Do NOT powdercoat the compressor. Unless the unit is torn down to just the shells the process will destroy it. Powdercoating temps are 475-500 degrees. Nothing on that unit is designed for those temps. Just have it polished. Actually you can do that your self provided you have the patients.
|
Nasty Notch
Member # 8863
|
posted
thanks for the info i think im jus leave it alone lol
|
68dustin
Member # 5388
|
posted
a little wet sanding and a buffer wheel will make it look alot better...
|
50Reasons
Member # 6452
|
posted
quote: Originally posted by copcar: Do NOT powdercoat the compressor. Unless the unit is torn down to just the shells the process will destroy it. Powdercoating temps are 475-500 degrees. Nothing on that unit is designed for those temps. Just have it polished. Actually you can do that your self provided you have the patients.
break it down if you do decide to do this otherwise you'll cook the seals...
|